Evaluation of EVA waste and PU-coated textiles as lightweight aggregate in Portland cement-based matrix

Authors

DOI:

https://doi.org/10.46421/enarc.v8i00.2929

Keywords:

EVA waste, PU coated textile waste, Lightweight aggregate, Partial replacement of conventional construction sand

Abstract

The present paper evaluates the influence of recycled lightweight aggregates (LA) based on EVA waste and PU-coated textiles as a partial replacement for conventional construction sand (CA) at 25% and 50% content. The compressive strength, water absorption and porosity of mortars were evaluated. The mortars containing 25% and 50% of AL showed a decrease in strength when compared to the control sample, however, they met the minimum standardized values. With the increase of the LA content, there was an increase in the amount of water absorbed by the samples. After 28 days, there was an increase in the porosity of the samples with 50%, due to the more irregular and porous surface of the LA compared to the CA.

Author Biographies

Luís Antonio Rodrigues Kroeff, Universidade Feevale

Possui Mestrado Profissional em Tecnologia de Materiais e Processos Industriais pela Universidade Feevale (2016). Atualmente é Coordenador de Contabilidade e Finanças do Instituto de Previdência e Assistência dos Servidores Municipais de Novo Hamburgo-RS (IPASEM), também é professor de ensino técnico profissionalizante na Escola Unialcance/Anhanguera (Dois Irmãos, RS). 

Alice Helena Meinhart, Universidade Feevale

Engenheira Civil. Mestrado em andamento.

Daiana Cristina Metz Arnold, Universidade Feevale

Doutora em Engenharia Civil pela Universidade do Vale do Rio dos Sinos (2021). Atualmente é Professora de ingressou no Curso de Engenharia Civil e Arquitetura e Urbanismo na Universidade Feevale. 

Marlova Piva Kulakowski, UNISINOS - Universidade Do Vale do Rio dos Sinos

Engenheira civil, professora e pesquisadora na Universidade Do Vale do Rio dos Sinos (UNISINOS)

Alexandre Silva de Vargas, Universidade Feevale

Engenheiro civil e professor na Universidade Federal de Santa Maria - RS.

References

AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM C 642/2021: Standard Test Method for Density, Absorption, and Voids in Hardened Concrete. DOI: 10.1520/C0642-21

ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 6136: Blocos vazados de concreto simples para alvenaria -Requisitos. Rio de Janeiro, 2016.

ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 7215: Cimento Portland - Determinação da resistência à compressão. Rio de Janeiro, 2019.

GADEA, J.; RODRÍGUEZ, A.; CAMPOS, P. L.; GARABITO, J.; CALDERÓN, V. Lightweight mortar made with recycled polyurethane foam. Cement and Concrete Composites, v. 32, n. 9, 2010, p. 672-677. DOI: 10.1016/j.cemconcomp.2010.07.017.

HANNAWI, K., PRINCE, W. & KAMALI-BERNARD, S. Efeito da Incorporação de Agregados Termoplásticos no Comportamento Físico, Mecânico e de Transferência de Materiais Cimentícios. Waste Biomass. 2010.

MEHTA, P. KUMAR; MONTEIRO, PAULO J.M. Concreto – Estrutura, Propriedades e Materiais. São Paulo. IBRACON, 2014.

MANSUR, A. A. P.; NASCIMENTO, O. L. do; MANSUR, H. S. Physico-chemical characterization of EVA-modified mortar and porcelain tiles interfaces. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1199-1208. DOI: 10.1016/j.cemconres.2009.07.020.

MOUNANGA, P.; GBONGBON, W.; POULLAIN, P.; TURCRY, P. Proportioning and characterization of lightweight concrete mixtures made with rigid polyurethane foam wastes. Cement & Concrete Composites. v. 30, p. 806 - 814, 2008.

POLARI FILHO, R. S.; DE MÉLO, A. B.; BARBOSA, N. P. II ENCONTRO TEMÁTICO MEIO AMBIENTE E EDUCAÇÃO AMBIENTAL, 2003.

ROCHA, F. de M. D. Aproveitamento de resíduos sólidos industriais em materiais alternativos na perspectiva da construção seca: Bloco EVA - Intertravamento e racionalização das alvenarias. 2008. Dissertação (Mestrado) -Curso de Pós-graduação em Engenharia Urbana, Centro de Tecnologia, Universidade Federal da Paraíba, João Pessoa, 2008.

SAIKIA, N.; BRITO, J. Use of plastic waste as aggregate in cement mortar and concrete preparation: a review. Construction and Building Materials, v. 34, p. 385 – 401. 2012.

SANTIAGO, E.; LIMA, P.; LEITE, M.; TOLEDO FILHO, R. Mechanical behavior of recycled light weight concrete using EVA wasteand CDW undermoderate. Revista IBRACON de Estruturas de Materiais, v.2, p. 211 – 221. 2009.

SOUSA, A. J. C. de. Aplicação de Argamassas Leves de Reboco e Assentamento em Alvenarias. Dissertação de Mestrado em Engenharia Civil. Faculdade de Engenharia da Universidade do Porto; Portugal, 2010.

TREIN, F.; VARGAS, A.; RODRIGUES, M.; GOMES, J. Avaliação do Comportamento Mecânico e Ambiental de Argamassas Alcali-ativadas contendo Resíduos à base de PU/EVA. Congresso Luso-Brasileiro de Materiais de Construção Sustentáveis CLB-MCS, Guimarães, Portugal, 2014. (A)

TREIN, F.; VARGAS, A.; RODRIGUES, M.; GOMES, J. Avaliação da Influência de Agregados Leves à base de resíduos de PU/EVA nas Propriedades Físicas das Argamassas Álcali-ativadas. Congresso Luso-Brasileiro de Materiais de Construção Sustentáveis CLB-MCS, Guimarães, Portugal. 2014. (B)

TREIN, F. Influência do Uso de Resíduos de EVA e de Têxteis Recobertos com Poliuretano como Agregado Leve em Argamassas Álcali-Ativadas. 2015. Tese (Doutorado em Tecnologia de Materiais e Processos Industrias) - Universidade FEEVALE, Rio Grande do Sul, 2015.

WANG, R.; MEYER, C. Performance of cement mortar made with recycled high impact polyestyrene. Cement & Concrete Composites, v. 34, p. 975 – 981.

Downloads

Published

25/10/2023

How to Cite

Kroeff, L. A. R., Meinhart, A. H., Arnold, D. C. M., Kulakowski, M. P., & Vargas, A. S. de. (2023). Evaluation of EVA waste and PU-coated textiles as lightweight aggregate in Portland cement-based matrix. ENCONTRO NACIONAL DE APROVEITAMENTO DE RESÍDUOS NA CONSTRUÇÃO, 8(00), 1–5. https://doi.org/10.46421/enarc.v8i00.2929

Issue

Vol. 8 (2023): VIII ENCONTRO NACIONAL DE APROVEITAMENTO DE RESÍDUOS NA CONSTRUÇÃO

Section

Aproveitamento de Resíduos

Most read articles by the same author(s)