Manufacturing polymeric composites based on waste and construction waste
DOI:
https://doi.org/10.46421/enarc.v8i00.3024Keywords:
Composites, Construction and demolition waste, Expanded polystyreneAbstract
Due to the growing concern about environmental issues, society increasingly demands sustainable products. Construction and demolition waste (CDW) is responsible for a large part of solid urban waste, causing a significant impact on the environment. In this context, research was carried out with the aim of developing polymeric matrix composites based on expanded polystyrene reinforced with RCD particles. The residues were characterized and incorporated into the expanded polystyrene in different proportions using the "Casting" method. The mixture was placed in molds and allowed to dry for 30 days. The results showed that composites with addition of 25% and 50% RCD had an average increase in axial compression strength of 26% and 36%, respectively. Composites with 5%, 10% and 15% RCD showed higher values of specific mass, water absorption and impact strength compared to pure polystyrene.
References
ALMEIDA, J. Viabilidade técnica do uso e econômica da produção do agregado de RDC em pavimentação de vias urbanas. 2015, 118p. Dissertação de mestrado em engenharia civil e ambiental. Universidade de Passo Fundo, Passo Fundo, 2015.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 15116: Agregados reciclados para uso em argamassas e concretos de cimento Portland – Requisitos e métodos de ensaios. Rio de Janeiro, 2021.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR NM 52: Agregado miúdo – Determinação de massa específica e massa específica aparente. Rio de Janeiro, 2002.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 9775: Agregado miúdo – Determinação do teor de umidade superficial por meio do frasco de Chapman – Método de ensaio. Rio de Janeiro, 2011.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 7973: Poliestireno expandido para isolação térmica - Determinação de absorção de água. Rio de Janeiro, 2007.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 8082: Espuma rígida de poliuretano para fins de isolação térmica - Determinação da resistência à compressão. Rio de Janeiro, 2016.
AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM 256: Standard Test Methods for Determining the Izod Pendulum Impact Resistance of Plastics. West Conshohocken, 2023.
AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM D570: Standard test method for water absorption of plastics. West Conshohocken, 2022.
AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM E23: Standard Test Methods for Notched Bar Impact Testing of Metallic Materials. West Conshohocken, 2022.
CABRAL, Antônio Eduardo Bezerra; SCHALCH, Valdir; DAL MOLIN, Denise Carpena Coitinho; RIBEIRO, José Luiz Duarte. Modelagem da resistência à compressão de concretos produzidos com agregados reciclados de RCD. Revista Minerva, São Carlos, v. 4, n. 1, p. 75-84, 2007.
CONCEIÇÃO, M. M. M. et al. Diagnóstico dos resíduos de demolição e construção no Brasil Brazilian Journal of Development, v. 7, n. 9, p. 87466-87481, 2021. Disponível: https://doi.org/10.34117/bjdv7n9-080
CONSELHO NACIONAL DO MEIO AMBIENTE (CONAMA). Resolução n º 307, de 05 de julho de 2002: Estabelece diretrizes, critérios e procedimentos para a gestão dos resíduos da construção civil. Diário Oficial da União, Brasília, DF, 17 jul. 2011.
COSTA, A.S.G, et al. Ensaios de tração e absorção de água em compósitos de resina poliéster e fibra de açaí.In: 21º CBECIMAT - Congresso Brasileiro de Engenharia e Ciência dos Materiais 09 a 13 de Novembro de 2014, Cuiabá, MT, Brasil.
GOMES. Jailton Weber Gomes,et al. Absorção de água e propriedades mecânicas de compósitos poliméricos utilizando resíduos de MDF. Polímeros, 27, 48-55, 2017.
GOMES, Jailton W. et al. Absorção de água e propriedades mecânicas de compósitos poliméricos utilizando resíduos de MDF. Polímeros, v. 27, p. 48-55, 16 mar. 2017. Disponível em: <http://www.scielo.br/pdf/po/v27nspe/0104-1428-po-0104-14281915.pdf>. Acesso em: 29 jun. 2023.
HAUS, Jason, ABRECON, V. Reciclagem de resíduos da construção civil e demolição. In: SEMINÁRIO NACIONAL DA RECICLAGEM DE RESÍDUOS DA CONSTRUÇÃO CIVIL E DEMOLIÇÃO, São Paulo 2015. Disponível em: http://www.acquacon.com.br/seminariorcd/index.php. Acesso em: 30 janeiro de 2023.
JOHN, Vanderley; AGOPYAN, Vahan. Reciclagem de resíduos da construção. In: SEMINÁRIO RECICLAGEM DE RESÍDUOS DOMICILIARES, São Paulo, 2000. Disponível em: www.reciclagem.pcc.usp.br. Acesso em: 19 abril de 2023.
MACHADO, Alan Rodrigues Teixeira, et al. Compósitos biodegradáveis a base de polihidroxibutirato-hidroxivalerato (PHB-HV) reforçados com resíduos do beneficiamento do café, Revista Matéria, 15 (2010) 400-404.
MONTEIRO FILHA, Dulce Corrêa; COSTA, Ana Cristina Rodrigues da; ROCHA, Érico Rial Pinto da. Perspectivas e desafios para inovar na construção civil. BNDES Setorial, Rio de Janeiro, n. 31, p. 353-410, mar. 2010.
SHACKELFORD, James (1996). Introduction to materials Science for engineers. New York,John Wiley & Sons.