ANÁLISES DE ARGAMASSAS DE REVESTIMENTO PRODUZIDAS COM REJEITO DE MINÉRIO DE FERRO
DOI:
https://doi.org/10.46421/entac.v17i1.1687Palavras-chave:
Coating mortars, Iron ore tailings, Mechanical propertiesResumo
Mining is one of the main sectors for the Brazilian economy and the state of Minas Gerais accounts for 35% of Brazilian mining. However, ore mining generates thousands of tons per day of diferents liquid, solid and sludge wastes. In this work, the objective was to replace part of Portland cement (PC) for calcined and raw iron ore tailings (IOT) in the production of cementlime mortars. Mortars were produced with PC, hydrated lime and sand, using a constant 1:2:9 (weight basis). The IOT samples were used in a raw state and also calcined at 500°C, both ground for 10 minutes. The cement was replaced by IOT in the following percentages: 0%, 10%, 20%, 40% and 60%. The water/binder ratio of each mortar was determined by the consistency index. Cylindrical specimens were molded to determine the water absorption by immersion, borehole index and bulk density, at 28 days. For the flexural tensile strength test, 40x40x160mm prismatic specimens were molded. All specimens remained in the mold for 48 hours and, after demolding, they were cured in a laboratory environment until the test date. The results showed that the substitution of the PC for IOT, until 60% in mortars, didn't modify their properties.
Referências
ABNT. NBR 7175: Cal hidratada - Requisitos. Rio de Janeiro, 2003.
____. NBR 9778: Argamassa e concreto endurecidos - Determinação da absorçãode água por imersão - Índice de vazios e massa específica. Rio de Janeiro, 1987.
____. NBR 13276: Argamassa para assentamento e revestimento de paredes e tetos -Preparo da mistura e determinação do índice de consistência. Rio de Janeiro, 2002.
____. NBR 13279: Argamassa para assentamento e revestimento de paredes e tetos -Determinação da resistência à tração na flexão e à compressão. Rio de Janeiro,2005.
____. NBR 13281: Argamassa para assentamento e revestimento de paredes e tetosRequisitos. Rio de Janeiro, 2005.
DEPARTAMENTO NACIONAL DE PRODUÇÃO MINERAL - DNPM. Anuário MineralBrasileiro: Principais Substâncias Metálicas / Coord. Geral W. F. Pinheiro, O. B. FerreiraFilho, C. A. R. Neves; Equipe Técnica por Marina Marques Dalla Costa... [et. Al.];Brasília: DNPM, 2016. 31 p.: il.
DUBAJ, E. Estudo comparativo entre traços de argamassa de revestimento utilizadasem Porto Alegre. 2000. 102 f. Dissertação (Mestrado) - Curso de Engenharia Civil,Universidade Federal do Rio Grande do Sul, Porto Alegre, 2000.
FONTES, W. C.; MENDES, J. C. SILVA, S. N.; PEIXOTO, R. A. F. Mortars for laying andcoating produced with iron ore tailings from tailing dams. Construction and BuildingMaterials, v. 112, p. 988 995, 2016.
FRANCO, L. C., SANTOS, D. H.; ROSA, P. P. G.; SILVA, G. J. B.; PEIXOTO, R. F. Aplicaçãode rejeitos de mineração como agregado para a produção de concreto. Anais do56º Congresso Brasileiro do Concreto. Campo Grande: IBRACON, 2014.
IBRAM - INSTITUTO BRASILEIRO DE MINERAÇÃO. Informações Sobre a EconomiaMineral Brasileira. Brasília, 2015.
____. Panorama da Mineração em Minas Gerais. Brasília: Grifo Design, 2016. 279 p.
Disponível em: <http://www.ibram.org.br/sites/1300/1382/00006212.pdf>. Acesso em:25 nov. 2017.
IPEA - Instituto de Pesquisa Econômica Aplicada. Secretaria de Assuntos Estratégicosda Presidência da República. Diagnóstico dos Resíduos Sólidos da Atividade deMineração de Substâncias Não Energéticas. Brasília: Livraria - Ipea, 2012. 40 p.
Disponível em: <http://ipea.gov.br/agencia/images/stories/PDFs/relatoriopesquisa/120814_relatorio_atividade_mineracao.pdf>. Acesso em: 25 nov. 2017.
MAGALHÃES, L. F.; MORAIS, I. S.; ESTEVES JUNIOR, M. A.; MELO, A. C.; MAIA, A. L. F.;BEZERRA, A. C. S. Resistência ao ataque ácido de cimento Portland com adição derejeito de minério de ferro. Anais do 59º Congresso Brasileiro do Concreto. BentoGonçalves : IBRACON, 2017.
Shettima, A. U., Hussin, M. W., Ahmad, Y., Mirza, J. Evaluation of iron ore tailings asreplacement for fine aggregate in concrete. Construction and Building Materials, v.120, p. 72 79, 2016.
PEIXOTO, R. A. F. Utilização de Rejeitos de Barragem de Minério de Ferro naConstrução Civil./ Relatório Técnico. Ouro Preto: UFOP, 2016. Disponível em: <http://www.reciclos.ufop.br/media/uploads/downloads/Relatorio_MPFFIOROTTI.pdf>. Acesso em 10 nov. 2017.
ZHAO, S., FAN, J., SUN, W. Utilization of iron ore tailings as fine aggregate in ultra-highperformance concrete. Construction and Building Materials, v. 50, p. 540 548, 2014.