ANÁLISE DA VIABILIDADE DO USO DE GARRAFA PET TRITURADA COMO SUBSTITUIÇÃO AO AGREGADO NATURAL EM ARGAMASSAS
DOI:
https://doi.org/10.46421/entac.v17i1.1690Palavras-chave:
Polyethylene Terephthalate (PET), Waste, Mortars, Recycled aggregateResumo
The main objective of this research is to evaluate the influence and viability of natural aggregates partial substitution by polyethylene terephthalate (PET) residues in mortars. Specifically, it was evaluated the properties of mortars in fresh and hardened state, with different PET waste granulometric composition. In order to achieve the work objectives, the aggregates were characterized and then an experimental matrix were developed. Mortars with 1:3 (cement: aggregate) mix proportion were produced. First of all, a reference mortar, only with natural aggregate, and then four mortars with different PET waste granulometry, called Flake, Powder, Fine and Mix. The results indicated that, in relation to mortar's workability, there was an influence of PET waste addition, probably related to the shape of the grains and a number of fines particles. It was observed a decrease in the flexural and compressive strength. Also, the mortar's density decreased as the granulometry with the higher number of fines was incorporated. Thus, among all the granulometry from PET waste incorporated in the mortars, the Flake appears to be one of the best alternatives for a more noble destination of the material, adding value and reducing environmental impacts.
Referências
AGOPYAN, V.; JONH, V. M. O desafio da sustentabilidade na construção civil. SãoPaulo: Blucher, 2011. (Série Sustentabilidade; v. 5) 141 p.
ALBANO, C; CAMACHO, N; REYES, J; FELIU, L; HERNANDEZ, M. Influence of contentand particle size of waste pet bottles on concrete behavior at different w/c ratios.
Waste Management, Caracas, v. 29, p.2707-2716, jul. 2009.
ALBANO, C; CAMACHO, N; HERNANDEZ, M; MATHEUS, A; GUTIERREZ, A. Influence ofscrap rubber addition to Portland I concrete composites: Destructive and nondestructivetesting. Composite Structures, Caracas, v. 71, n., p.439-446, jul. 2005.
ALMEIDA, M. O. de; FERRARI JÚNIOR, M. J.; OLIVEIRA, D. D. de; ATHAYDE JÚNIOR, G.
B. Uso de areia de PET na fabricação de concretos. In: congresso brasileiro de ciência e tecnologia em resíduos e desenvolvimento sustentável. Florianópolis, 2004.p. 2 11.
ABNT ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS NBR NM 5753: CimentoPortland - Ensaio de pozolanicidade para cimento Portland pozolânico.
Apresentação. Rio de Janeiro, 2016______.NBR 7211: Agregados para concreto Especificação. Rio de Janeiro, 2009.
______.NBR 13.276: Argamassa para assentamento e revestimento de paredes etetos Determinação do índice de consistência. Rio de Janeiro, 2016.
______. NBR 13.278: Argamassa para assentamento e revestimento de paredes etetos Determinação da densidade de massa e do teor de ar incorporado. Rio deJaneiro, 2005.
______.NBR 13.279: Argamassa para assentamento e revestimento de paredes etetos Determinação da resistência à tração na flexão e à compressão. Rio deJaneiro, 2005.
______.NBR 13.280: Argamassa para assentamento e revestimento de paredes etetos Determinação da densidade de massa aparente no estado endurecido. Riode Janeiro, 2005.
______.NBR 15.259: Argamassa para assentamento e revestimento de paredes etetos Determinação da absorção de água por capilaridade e do coeficiente decapilaridade. Rio de Janeiro, 2005.
CARNEIRO, E. P.; REIS, J. M. L. Mechanical properties of polymer mortar containingpet waste aggregates. In: 21st Brazilian Congress of Mechanical Engineering, 2011,Natal: ABCM, 2011. p. 1 - 6.
OLIVEIRA, M. C. B. R. de. Gestão de resíduos plásticos pós-consumo: perspectivaspara a reciclagem no Brasil. 2012. 104 f. Dissertação (Mestrado) - Curso dePlanejamento Energético, UFRJ, Rio de Janeiro, 2012.