USO DO RCV COMO SUBSTITUINTE PARCIAL AO AGLOMERANTE E AGREGADO MIUDO EM ARGAMASSAS DE REVESTIMENTO
Palavras-chave:
CBW, Coating mortar, Sustainability, Architecture technologyResumo
The search for more sustainable forms of the life has reflected directly in civil construction industry, for being, economically speaking, one of the most important to the country, although, is highly degrading to the environment, by either resource extraction, or the generation of waste. The ceramic industry fits in this picture, by the extraction of clay and the generation of the ceramic brick waste, residue result after burning problems and breaks ceramic parte. In search of an alternative to a sustainable disposal, and also, a reduction of consumption of raw materials in construction, this study evaluates the use of CPR in coating mortars. For this, it was made a mortar, called 5C, with replacement of 5% of the binder by CPR and one, called 10A, with 10% substitution by aggregate, plus a mortar without addition of residue for reference. The materials used were characterized, and the specimen passed through test of axial compression and traction by diametral, in order to evaluate the performance of the mortars. The results showed that the mortars that used waste are quite similar that the reference mortar, proving the feasibility of the use of residual mortar.
Referências
Associação Brasileira de Normas Técnicas. Argamassa para assentamento e
revestimento de paredes e tetos - Determinação da resistência à tração na flexão e
compressão: NBR 13279, Rio de Janeiro, 2005.
____. Agregados – Determinação da massa unitária e volume de vazios: NBR NM 45.
Rio de Janeiro, 2006.
____. Agregados - Determinação da Composição granulométrica: NBR NM 248. Rio
de Janeiro, 2003.
____. Cimento Portland - Resistência a Compressão: NBR 7215. Rio de Janeiro, 1996.
____. Cimento Portland e outros materiais em pó – Determinação da massa
específica: NBR NM 23. Rio de Janeiro, 2001.
____. Concretos e argamassas - Determinação da resistência à tração por
compressão diametral: NBR 7222. Rio de Janeiro, 2011.
Associação Brasileira de Empresas de Limpeza Pública e Resíduos Especiais –
ABRELPE. Panorama dos resíduos no Brasil, 2015. Disponível em:
http://www.abrelpe.org.br/panorama_edicoes.cfm
ARAÚJO, R. A., Influência da utilização de resíduo de cerâmica vermelha nas
propriedades de argamassas mistas. Dissertação de Mestrado em Engenharia Civil,
Universidade Federal do Rio Grande do Norte, Programa de Pós-Graduação em
Engenharia Civil. 95f; Natal, RN. 2017.
CABRERA, F. G. C.; SOBERÓN, J. M. G.; SÁNCHEZ, J. L. A.; REA, S. P. A.; HIGUERA, R. C.,
Mechanical properties of mortar containig recycled ceramic as fine aggregate
replacement. Revista de la Construcción, vol. 14, n. 3, p. 22-29, dez. 2015.
CARDOSO, J. T. O., FORTI, N. C. S. Estudo para aplicação de resíduos de cerâmica
vermelha na produção de argamassa cimentícia. ENCONTRO DE INCIAÇÃO EM
DESENVOLVIMENTO TECNOLOGICO E INOVAÇÃO, 5, Campinas, 2015. Anais do V
Encontro de iniciação em desenvolvimento tecnológico e inovação.
MENDES, B.S.; BORJA, E.V. Estudo experimental das propriedades físicas de
argamassas com adição de resíduos de cerâmicas vermelhas recicladas. Rio
Grande do Norte, 2007. Trabalho técnico- CEFET-RN, 2007. Disponível em: <http://www2.ifrn.edu.br/ojs/index.php/HOLOS/article/ viewFile/127/115>. Acesso em:
ago. 2015.
PINHEIRO, I. S. Beneficiamento e caracterização de resíduos gerados na produção
de blocos visando à aplicação como adição pozolânica. 2008, 152 p. Dissertação
(Mestrado em Engenharia Civil) – Escola de Engenharia, Universidade Federal de
Minas Gerais, 2008.