Evaluation of the use of alternative materials in the production of stabilized mortar: metakaolin and Ethylene Vinyl Acetate (EVA) as sustainable options
DOI:
https://doi.org/10.46421/entac.v20i1.6280Keywords:
EVA (Ethylene Vinyl Acetate) residue, Lightweight aggregat, Metakaolin. SustainabilityAbstract
The research deals with the possibility of using alternative materials in the production of stabilized mortar, made in a dosing plant and has its workability between 48 and 72 hours, favoring the productivity of the work. The substitution of 20% by mass of Portland cement by Metakaolin (MC) and fine aggregate by Ethylene Vinyl Acetate (EVA) residue, in volume, in proportions of 10%, 20% and 30%, were analyzed. The mortar tests were performed under stabilization conditions of 0 and 48 hours. The resulting mortars were subjected to tests in the fresh state (Flow table, Squeeze flow, fresh mass density and incorporated air content). The results indicated that the MC reduces the consistency of the mortars in the consistency test depending on their stabilization time and increases the incorporated air content. Mortars with EVA showed good consistency at 0h and 48h, evidenced by rheological parameters. All mortars containing EVA showed increased incorporated air content, decreased fresh mass density, compared to the reference. It is worth mentioning that the properties of mortars varied according to the stabilization times.
References
ANTONIAZZI, J. P.; Vaz, L. V.; MOHAMAD, G.SCHMIDT, R.P.B.; MODLER, L. E. Influência do procedimento de mistura dos aditivos nas propriedades das argamassas estabilizadas. XIII Simpósio Brasileiro de Tecnologia das Argamassas, Goiânia, 2019.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS (ABNT). NBR 13278: Argamassa para assentamento e revestimento de paredes e tetos – determinação da densidade de massa e do teor de ar incorporado. Rio de Janeiro, 2005a.
___________.. NBR 16605: Cimento Portland e outros materiais em pó – Determinação da massa específica. Rio de Janeiro, 2017.
___________ . NBR 16972: Agregados - Determinação da massa unitária e do índice de vazios. Rio de Janeiro, 2021a.
___________. NBR 16916: Agregado miúdo - Determinação da densidade e da absorção de água. Rio de Janeiro, 2021b.
___________. NBR 16697: Cimento Portland – Requisitos. Rio de Janeiro, 2018.
___________ . NBR 17054: Agregados - Determinação da composição granulométrica - Método de ensaio. Rio de Janeiro, 2022.
___________ .NBR 12653: Materiais pozolânicos — Requisitos. Rio de Janeir0, 2014.
___________. NBR 15894-1: Metacaulim para uso com cimento Portland em concreto, argamassa e pasta - Parte 1: Requisitos. Rio de Janeiro, 2010a.
___________. NBR 15839: Argamassa de assentamento e revestimento de paredes e tetos – Caracterização reológica pelo método squeeze-flow. Rio de Janeiro, 2010b.
___________. NBR 16541: Argamassa para assentamento e revestimento de paredes e tetos – Preparo da mistura para a realização de ensaios. Rio de Janeiro, 2016a.
___________. NBR 13276: Argamassa para assentamento e revestimento de paredes e tetos – determinação do índice de consistência. Rio de Janeiro, 2016b.
CARDOSO, F.A. ; PILEGGI, R. G. ; JOHN, V. M. . Squeeze-flow aplicado a argamassas de revestimento: Manual de Utilização. Boletim Técnico da Escola Politécnica da USP. BT/PCC , v. 1, p. 1- 29, 2010.
DA COSTA, M. do R. de M. M.; PINTO, M. C. C.; PESSANHA, M. D., ;TREVISAN, D. B.; HERZER, P. H. (2021). Argamassas contendo resíduos a base de EVA e poliéster como agregado leve paper 818 / Mortars containing EVA and polyester based waste as lightweight paper 818 aggregate. Brazilian Journal of Development, 7(1), 8421–8436. https://doi.org/10.34117/bjdv7n1-571.
FARINHA, C.; DE BRITO, J.; VEIGA, R. Incorporation of fine sanitary ware aggregates in coating mortars. Construction and Building Materials, v. 83, p. 194-206, 2015.
GUIMARÃES, C. C.; ANDRADE, É. S. Propriedades de argamassas com EVA (ethylene vinyl acetate) em substituição parcial ao agregado. REEC - Revista Eletrônica de Engenharia Civil, Goiânia, v. 13, n. 1, 2017. DOI: 10.5216/reec.v13i1.40167. Disponível em: https://revistas.ufg.br/reec/article/view/40167. Acesso em: 24 maio. 2023.
GUINDANI, E. N. Argamassa estabilizada para revestimento: avaliação da influência da adição de finos nas propriedades do estado fresco endurecido Florianópolis, 2018. 146 f. Dissertação (Mestre em Engenharia Civil) - Centro Tecnológico, Universidade Federal de Santa Catarina, Florianópolis, 2018.
JACKIEWICZ-REK, W.; ZAŁĘGOWSKI, K.; GARBACZ, A.; BISSONNETTE, B. Properties of cement mortars modified with ceramic waste fillers. Procedia Engineering, 108, 681-687. 2015.
LAURENTINO, R. N. A. Estudo da argamassa estabilizada para assentamento com adição mineral de metacaulim. Universidade Federal da Campina Grande (UFCG). Campina Grande : s.n., 2019.
MANSUR, A. A. P. Mecanismos Físicos- químicos de Aderência na Interface Argamasico-Químicossa Modificada com Polímeros/Cerâmica de Revestimento. 2007. 357 f. Tese (Doutorado) - Curso de Engenharia Metalúrgica e de Minas, Universidade Federal de Minas Gerais, Belo Horizonte, 2007.
MATOS, Paulo Ricardo de; et al. Estudo da utilização de argamassa estabilizada em alvenaria estrutural de blocos de concreto. 2013. Trabalho de Conclusão de Curso. Universidade Federal de Santa Catarina, Florianópolis, 2013.
OLIVEIRA, V. C.. Estudo comportamental da formulação, dos requisitos, e das propriedades das argamassas estabilizadas de revestimento. 2017. xxii, 245 f., il. Dissertação (Mestrado em Estruturas e Construção Civil)—Universidade de Brasília, Brasília, 2017
PAULINO, I. M.. Propriedades de argamassa estabilizada contendo metacaulim e resíduo de tijolo cerâmico. 2020. 72f. Trabalho de Conclusão de Curso (Monografia), Curso de Bacharelado em Engenharia Civil, Centro de Tecnologia e Recursos Naturais, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2020. Disponível em: . Acesso em: 10 Out. 2022.
ROCHA, F. M. D. Aproveitamento de resíduos sólidos industriais em materiais alternativos na perspectiva da construção seca: Bloco Eva - intertravamento e racionalização das alvenarias. 2008. 110 f. Dissertação (Mestrado em Engenharia Urbana) - Universidade Federal da Paraíba, João Pessoa, 2008.
ROCHA, G. G. N. Caracterização microestrutural do metacaulim de alta reatividade. Minas Gerais: Dissertação de Mestrado em Engenharia Metalúrgica e de Minas – Universidade Federal de Minas Gerais, 2005.
ROSSIGNOLO, J.A. Concreto leve estrutural: produção, propriedades, microestrutura e aplicações. São Paulo, PINI, 2009.
SILVA, I. C. Argamassa estabilizada para assentamento contendo etileno acetato de vinila (EVA) e metacaulim. 59 f. Trabalho de Conclusão de Curso. Graduação em Engenharia Civil. Universidade Federal de Campina Grande – UFCG. Campina Grande, PB. 2023.
SILVA, I. C.; Azerêdo, A. F. N. . Argamassa estabilizada contendo metacaulim. Anais do VII CONAPESC... Campina Grande: Realize Editora, 2022. Disponível em: . Acesso em: 27/05/2023
SILVA, D. A.; ROMAN, H. R.; GLEIZE, P. J. P. Evidences of chemical interaction between EVA and hydrating Portland cement. Cement and Concrete Research, v. 32, n. 9, p. 1383-1390, Sep. 2002.
SUPRENANT, B. A. Ready Mixed Mortar Has More Life. Masonry Construct., v. 1, n. 4, p. 173, EUA. 1988. Disponível em: File:///E:/Downloads/Concrete%20Construction%20Article%20PDF%20Ready%20Mixed%20Mortar%20Ha s%20More%20Life.pdf. Acesso em: 17 Abril. 2023.