AVALIAÇÃO EXPERIMENTAL DE SUBPRODUTOS COMO PRECURSORES NO DESENVOLVIMENTO DE SISTEMAS ÁLCALI ATIVADOS
DOI:
https://doi.org/10.46421/entac.v18i.991Keywords:
Precursors, Activated alkali systems, Alternative cementsAbstract
The use of alternative cements is intensified in civil construction, since the production of Portland cement emits considerable amounts of CO2, due to the clinker burning. The activated alkali systems are a proposal, where, the conventional binder is replaced by precursors, which are mostly industrial waste or by-products, which together aim to minimize environmental impacts. The present study aimed to evaluate the residues heavy ash (CZP), rice husk ash (CCA) and red mud (LV), through experimental tests the capacity of these to be precursors in the development of activated alkali systems. The research was designed to characterize and test precursors with drying and / or calcination processing, seeking to improve the material's microstructure. The pH test in solution for 24 hours, X-ray diffraction (XRD) and X-ray dispersion energy (EDX) were applied to these. The results showed that all precursors obtain alkaline pH, a factor that contributes to the interaction of reactivity in chemical reactions, however, CCA shows interesting results, a larger specific surface that contributes to reactivity, composed of 92.74% silica, however, absence of alumina. It is concluded that the CCA stands out as a precursor to the binary composition of activated alkali systems.
References
ABNT ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 13276: Argamassa para assentamento e revestimento de paredes e tetos ― Determinação do índice de consistência. Rio de Janeiro, 2016.
______. NBR NM 76: Cimento portland - Determinação da finura pelo método de permeabilidade ao ar (Método de Blaine), Rio de Janeiro. 1996.
______. NBR NM 23: Cimento portland - Determinação e massa específica. Rio de janeiro. 2000.
______. NBR NM 248: Agregados - Determinação da composição granulométrica. Rio de Janeiro, 2003.b.
APOLONIO, P. H.,, J. S. LIMA, J. S., MARINHO, E. P., NOBREGA, A. C.V., FREITAS, J. C. O. Produção de geopolímeros utilizando cinza da casca de arroz como fonte complementar de sílica.
Cerâmica. V. 66. Nº 378. 2020.
BRITO, W. da S., BRUM, S. M., SILVA, A.L. M. F., FELIPE, A. M. P. F., SOUZA, J. A. da S. Avaliação do comportamento reológica e mecânico de geopolímero sintetizado com reaproveitamento de resíduo. Revista Matéria. V. 23. N. 03. 2018HWANG, C-L.; HUYNH, T-P. Effect of alkali-activator and rice husk ash content on strength development of fly ash and residual rice husk ash-based geopolymers. Construction and Building Materials. V. 101. P. 1–9. 2015.
MANFROI, E. P. Avaliação da lama vermelha como material pozolânico em substituição ao cimento para produção de argamassas. 2009. 152p. Dissertação (Mestrado em Engenharia Civil). Programa de Pós-Graduação em Engenharia Civil - Universidade Federal de Santa Catarina, Florianópolis. 2009.
NADOUSHAN, M. J.; RAMEZANIANPOUR, A.A. The effect of type and concentration of activators on flowability and compressive strength of natural pozzolan and slag-based geopolymers. Construction and Building Materials. V. 111. P. 337–347. 2016.BRAYNER, A. R. A.; MEDEIROS, C. B. Incorporação do tempo em SGBD orientado a objetos. In: SIMPÓSIO BRASILEIRO DE BANCO DE DADOS, 9., 1994, São Paulo. Anais... São Paulo: USP, 1994. p. 16-29.
PALOMO, A.; KRIVENKO, P.; GARCIA-LODEIRO, I.; KAVALEROVA, E.; MALTSEVA, O.; FERNÁNDEZJIMÉNEZ, A. A review on alkaline activation: new analytical perspectives. Materiales de Construcción. V. 64. Nº. 315. 2014.
SHI, C.; FERNÁNDEZ JIMÉNEZ, A.; PALOMO, A. New cements for the 21st century: The pursuit of an alternative to Portland cement. Cement and Concrete Research. V. 41. P. 750–763. 2011.