INFLUÊNCIA DE FIBRAS DE POLIPROPILENO NA PROPRIEDADE DE ADERÊNCIA EM ARGAMASSAS DE REVESTIMENTO
DOI:
https://doi.org/10.46421/entac.v17i1.1339Keywords:
Coating mortar, Polypropylene’s Fibers, Adhesion’s propertyAbstract
Mortar coatings comprise several functions, however, it's also associated to pathologies. Cracking and loss of adhesion of a mortar coating may be associated by the retraction effects. In order to solve those problems, fibers can be incorporated in the mortar, which tends to act by making it difficult to propagate cracks, helping in tension spreading. In this way, this paper aims to evaluate the influence from the polypropylene’s fiber on adhesion’s property of coating mortar. For the evaluation, three polypropylene fiber concentrations (500, 1000 and 1500 g/m[1]) were tested in a mixed mortar of cement and lime 1: 0.5: 6 (by volume). The mortars were applied in two thicknesses, 30 and 50 mm, on the surface of the concrete block prisms and the properties measured were density, consistency index, water retention, the normal stress supported on the flexure and compression tests and adhesion strength. It has been verified that the coating with polypropylene's fiber presented higher adhesion strength for both thickness. Also the values of the mechanics behavior for both concentrations, 1000 and 1500 g/m3, were very similar. To conclude the 1000 g/m3 presented higher resistance with lower consumption becoming the best option.
References
ABNT ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 7200: Execução de revestimento de paredes e tetos de argamassas inorgânicas - Procedimento. Rio de Janeiro, 1998.
AGOPYAN, V.; JOHN, V. M. Introdução a materiais reforçados com fibras e a tecnologia de CRV. In: Simpósio internacional componentes e sistemas construtivos em cimento reforçado com fibras de vidro, 2000, São Paulo. Anais... São Paulo, 2000.
BASTOS, P. K. X. Retração e desenvolvimento de propriedades mecânicas de argamassas mistas de revestimento. 2001, 172p. Tese (Doutorado), EscolaPolitécnica, Universidade de São Paulo. São Paulo, 2001.
BENTUR, A.; MINDESS, S. Fibre reinforced cementitious composites. 2. ed. United Kingdon: Barking Elsevier, 2007.
GUO-ZHONG, L.; SHUAI, Z. Proportioning Design and Mechanical Properties Research of Polypropylene Fiber and Polymer Emulsion Reinforced Cement Mortar. Journal OfMaterials In Civil Engineering, [s.l.], v. 22, n. 3, p.223-226, mar. 2010. American Society of Civil Engineers (ASCE). http://dx.doi.org/10.1061/(asce)0899-1561(2010)22:3(223).
JOHN, V. M. Repensando o papel da cal hidratada nas argamassas. In: SIMPÓSIO BRASILEIRO DE TECNOLOGIA DAS ARGAMASSAS, 5., 2003, São Paulo. Anais. São Paulo: 2003. p. 47 - 62.
MONTE, R.; BARROS, M. M. S. B.; FIGUEIREDO, A. D. Avaliação da influência de fibras de polipropileno na resistência de aderência de revestimentos de argamassa. In: Congresso Português de Argamassas de Construção, 4., 2012, Coimbra. Anais... Lisboa: Associação Portuguesa dos Fabricantes de Argamassas e ETICS, 2012. p. 1 - 12.
SIQUEIRA, J. E. L. de. Utilização de fibras naturais e sintéticas em argamassas de revestimento de alvenaria: estudo comparativo de desempenho. 2006. 217 f. Dissertação (Mestrado) - Curso de Engenharia Civil, Universidade Federal de Santa Catarina, Florianópolis, 2006.
TISCOSKI, B. L.; ANTUNES, E. G. P. Análise do efeito da adição de fibras de polipropileno na resistência de aderência à tração em argamassa de revestimento. In: UNESC, 2016, Florianopolis. Anais... Florianopolis: 2016. p 1-19.
WU, Y. et al. Surface-treated polypropylene fiber for reinforced repair mortar cementitious composites. Composite Interfaces, [s.l.], v. 21, n. 9, p.787-796, 7 out. 2014. Informa UK Limited. http://dx.doi.org/10.1080/15685543.2014.960320