AVALIAÇÃO DO GRAU DE HIDRATAÇÃO AO LONGO DO TEMPO DE ARGAMASSAS ESTABILIZADAS POR PERDA AO FOGO
Keywords:
Ready Mix mortar, Mortar, Degree of Hydration, Hydration stabilizing admixturesAbstract
The mortars were produced with the same ratio of water/ dry materials and the same content of air-entrained admixtures, while three contents of hydration stabilizing admixtures and a mortar without this admixture were evaluated. The ready mix mortars were characterized in the fresh state through the consistency index, specific gravity and air entrained content. In the hardened state, the evaluation of the degree of hydration by ignition loss were evaluated at the ages of 28, 42 and 56 days. The results obtained demonstrate there is no influence of the admixture content of hydration stabilizing on the properties of the mortars in the fresh state. In relation to the degree of hydration of the mortars, there was an increase of the hydrated compounds for the mortars without hydration stabilizing admixtures and the influence of the hydration stabilizing admixtures content. However, for mortars with a hydration stabilizing admixtures, small increment in the degree of hydration was observed in relation to the age of the mortars, in relation to the determined parameters.
References
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS (ABNT). NBR NM 46: Agregados:Determinação do material fiRio de Janeiro, 2003.
______. NBR NM 52: Agregados: Determinação da massa específica e massaespecífica aparente. Rio de Janeiro, 2009.
______. NBR NM 248: Agregados - Determinação da composição granulométrica. Riode Janeiro, 2003.
______. NBR 7215: Cimento Portland Determinação da resistência à compressão.Rio de Janeiro, 1996.
______. NBR 13276: Argamassa para assentamento e revestimento de paredes etetos Determinação do índice de consistência. Rio de Janeiro, 2005.
______. NBR 13278: Argamassa para assentamento e revestimento de paredes etetos determinação da densidade de massa e do teor de ar incorporado. Rio deJaneiro, 2005.
BAUER, B.; OLIVEIRA, V. C. Comportamentos e propriedades das argamassasestabilizadas de revestimento. In: X Simpósio Brasileiro de Tecnologia de Argamassa -SBTA. São Paulo, 2017. AnaisCASALI, J. M.; MELO, F. D.; SERPA, V. C.; OLIVEIRA, A. L.; BETIOLI, A. M.; CALÇADA, L.
M. L. Influence of cement type and water content on the fresh state properties ofready mix mortar. Ambiente Construído. v. 18. nº2. 2018.
FIORAVANTE, E. V. Influência dos aditivos nas propriedades de argamassasestabilizadas. Ponta Grossa, 2014. Trabalho de conclusão de curso (Engenharia deCivil) Universidade Estadual de Ponta Grossa, Ponta Grossa. 2014.
GONÇALVEZ, J. P., TOLEDO FILHO, R. D., FAIRBAIRN, E. M. R. Estudo da hidratação depastas de cimento Portland contendo resíduo cerâmico por meio de análisetérmica. Ambiente Construído, Porto Alegre, v. 6, n. 4, p 83-94 out./dez. 2006.
LAM, L.; WONG, Y.L.; POON, C.S. Degree of hydration and gel/space ratio of highvolumefly ash/cement systems. Cement and Concrete Reserch. v. 30, p. 747-56. 2000.
MASUELA, F. B.; CAMARINI, G. Avaliação do grau de hidratação do cimento porperda ao fogo. In: XVI Encontro Nacional de Tecnologia do Ambiente Construído.São Paulo, 2016. Anais 6.
NARMLUK, M., NAWA, T. Effect of fly ash on the kinetics of Portland cement hydrationat different curing temperatures. Cement and Concrete Research. v. 41. p. 579-89.2011.
NEVILLE, A. M., BROOKS, J. J. Tecnologia do concreto. Editora Bookman. 2ª Edição.2013.
RUPPENTHAL, S. M.; PELISSER, F. Estudo de Argamassas de Revestimento com Inibidoresde Hidratação. 2012. Disponível em:<http://200.18.15.27/bitstream/1/1158/1/Suelem%20Michels%20Ruppenthal.pdf>.Acesso em: 16 nov. 2017.
TAYLOR, H. F. W. Cement chemistry. 2. ed. London: Thomas Telford, 1997.